dc.description.abstractEceng gondok (Eichhornia crassipes) merupakan tumbuhan air yang mengandung lignoselulosa dan populasinya sangat melimpah. Penelitian ini bertujuan untuk mengevaluasi pengaruh kadar perekat UF dan ukuran partikel terhadap kualitas papan partikel eceng gondok. Kadar perekat yang digunakan adalah 8%, 10% dan 12% serta ukuran partikel yang digunakan adalah partikel kasar (tertahan saringan 10 mesh) dan partikel halus (lolos saringan 10 mesh). Papan partikel dibuat dengan ukuran 25 cm x 25 cm x 1 cm dengan target kerapatan yang ditetapkan adalah 0,8 g/cm3. Papan dikempa dengan dengan suhu 130oC selama 10 menit pada tekanan 30 kg/cm3. Hasil penelitian menunjukkan pengaruh kadar perekat dan ukuran partikel terhadap sifat fisis papan partikel telah memenuhi standar JIS A 5908 (2003) sedangkan pengembangan tebal belum memenuhi standar. Sifat mekanis yang dihasilkan untuk MOE dan MOR belum memenuhi standar sedangkan IB (partikel kasar) telah memenuhi standar. Kadar perekat dan ukuran partikel berpengaruh nyata terhadap kerapatan dan MOR papan partikel. Perlakuan yang paling optimal adalah perlakuan kadar perekat 12% dengan ukuran partikel kasar (KC).en_US
dc.description.abstractWater hyacinth (Eichhornia crassipes) is water plant containing lignocelluloses and the population is very abundant. The purpose of this study was to evaluate the effect of formaldehyde adhesives content and size particle on the physical and mechanical properties of water hyacinth particleboard. The adhesive content in this study were 8%, 10% and 12% and the size particle were consisted of coarse particle (retained 10 mesh sieve) and sized fine particle (wriggle out 10 mesh sieve). Particleboard were made with size 25 cm x 25 cm x 1 cm with target density 0,8 g/cm3. The particleboards were pressed by 130oC temperature for 10 minutes with pressure 30 kg/cm3. The results showed that adhesives content and size particle have influenced of physical properties and fulfilled the standard JIS A 5908 (2003) except the thickness swelling. However adhesives content and size particle have influenced of mechanical properties namely internal bond (IB), modulus of elasticity (MOE) and modulus of rupture (MOR). Adhesives content and size particle have significant influence on moisture content and modulus of rupture (MOR). Optimal condition was attained by combination adhesives content 12% and sized coarse particle (KC).en_US
dc.language.isoiden_US
dc.subjectWater Hyacinthen_US
dc.subjectParticleboarden_US
dc.subjectAdhesives Contenten_US
dc.subjectSize Particleen_US
dc.titleKualitas Papan Partikel Dari Eceng Gondok (Eichhornia crassipes) dengan Variasi Kadar Perekat Urea Formaldehida dan Ukuran Partikelen_US
dc.typeStudent Papersen_US


Files in this item

Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record