Show simple item record

dc.contributor.advisorSembiring, Timbangen
dc.contributor.advisorHumaidi, Syahrul
dc.contributor.authorHarahap, Elsa Eka Putri
dc.date.accessioned2015-03-10T07:04:45Z
dc.date.available2015-03-10T07:04:45Z
dc.date.issued2015-03-10
dc.identifier.otherZulhelmi
dc.identifier.urihttp://repository.usu.ac.id/handle/123456789/44527
dc.description100801023en_US
dc.description.abstractTelah dilakukan penelitian pembuatan dan karakterisasi mekanik dan akustik papan komposit poliester dengan pengisi serat bambu. Komposit ini dibuat dengan komposisi serat bambu yaitu 5%, 10%, 15%, 20%, 25%, masing-masing ditambahkan katalis MEKPO 1 % dari volume polyesternya sebagai pengeras, kemudian dituang pada cetakan dan dipress 20 menit pada suhu 50 0C. Hasil komposit serat bambu meliputi nilai densitas dari 0,74 gr/cm3 sampai 1,03 gr/cm3, nilai kuat tarik dari4,33 N/mm2 sampai 9,05 N/mm2, nilai kuat impak dari 54,67 kJ/m2 sampai 147,82 kJ/m2. Hasil yang diperoleh sesuai dengan Standar Industri Jepang (JIS A5905-2003) . Hasil uji koefisien serap bunyi menunjukkan bahwa penambahan serat bambu akan meningkatkan nilai koefisien serap bunyi dimana nilai optimum diperoleh pada komposisi serat bambu 25 % dengan frekuensi 2000 Hz.en_US
dc.description.abstractHasconducted research and manufacture of mechanical and acoustic characterization of polyester composite boards with bamboo fiber filler. The composite is made with bamboo fiber composition of 5%, 10%, 15%, 20%, 25%, respectively MEKPO added catalyst 1% of the volume polyester as speaker, then poured in molds and pressed 20min at 500C. Results include bamboo fiber composite density values of 0.74gr/cm3to1.03gr/cm3, tensile strength values of 4, 33N/mm2to9.05N/mm2, impac strength of54.67kJ/m2to 147, 82kJ/m2. The results obtainedin accordance with the Japanese Industrial Standard (JIS A5905-2003). Sound absorption coefficient ofthe test results showed that the addition of bamboo fiber will improvethe sound absorption coefficient where the optimum value is obtained at the composition of25% bamboo fiber with a frequencyof 2000Hz.en_US
dc.language.isoiden_US
dc.subjectComposite Fiberboardsen_US
dc.subjectPolyesteren_US
dc.subjectBamboo Fiberen_US
dc.titlePembuatan dan Karakterisasi Mekanik dan Akustik Papan Komposit Polyester dengan Pengisi Serat Bambuen_US
dc.typeStudent Papersen_US