| Title: | Pembuatan Magnet Permanent Ba-Hexa Ferrite (Bao.6fe2o3) Dengan Metode Koopresipitasi Dan Karakterisasinya |
| Authors: | Afza, Erini |
| Advisors: | Ginting, Herli |
| Issue Date: | 23-Jun-2011 |
| Abstract: | Magnet permanen dibuat dari bahan keramik berbasis oksida besi seperti hexagonal
ferrite BaO.6Fe2O3. Bahan magnet ini memiliki kemampuan remanensi sebesar 2000
G dan koersivitas sebesar 1457 Oe. Pembuatan magnet permanen Barium hexa ferrite
diawali dengan pembuatan serbuk BaO.6Fe2O3 melalui metode koopresipitasi dengan
menggunakan bahan baku BaCl2 ,dan FeCl3 . Serbuk tersebut dikalsinasi pada suhu
900oC selama 2 jam, kemudian ditambahkan bahan perekat Poly Vinyl Alcohol (PVA)
dan dicetak kering dengan tekanan 70 kg/cm2 . Hasil cetakan berupa pellet dengan
diameter 2,39 cm x 0,49 cm. Selanjutnya dilakukan proses sintering dengan
menggunakan tungku listrik pada suhu 1000oC - 1100oC dengan interval 50oC. Pada
setiap suhu sintering ditahan selama 2 jam. Sampel yang telah disintering kemudian
dikarakterisasi sifat fisik (densitas dan porositas), dianalisis struktur kristalnya dengan
XRD, dimagnetisasi dan diukur kurva histerisisnya. Dari hasil karakterisasi diperoleh
hasil yang terbaik yaitu pada kondisi suhu sintering 1100oC, dengan nilai densitas =
3,82 g/cm3, porositas = 28,21%, fasa yang terbentuk seluruhnya adalah BaO.6Fe2O3,
memiliki Br = 1802,76 G dan Hc = 892 Oe. |
| Abstract (other language): | Permanent magnets made by iron oxide-based ceramic material as hexagonal ferrite
BaO.6Fe2O3. This magnetic material has the ability remanence of 2000 G and the
coercivity of 1457 Oe. Fabrication of barium hexa ferrite permanent magnets begins
with the manufacture of powder BaO.6Fe2O3 through coopresipitation method using
raw materials BaCl2, and FeCl3. The powder is calcined at a temperature of 900oC
for 2 hours, then added adhesive Poly Vinyl Alcohol (PVA) and dry pressing with
pressure 70 kg/cm2 The mpld form of pellets with a diameter of 2.39 cm x 0.49 cm.
Furthermore, the sintering process is carried out by using electric furnace at
temperatures 1000oC - 1100oC with 50oC intervals. At each sintering temperature
held for 2 hours. Sintering samples were then characterized the physical properties
(density and porosity), its crystal structure analyzed by XRD, magnetized and
measured curves histerisisnya From the characterization results obtained best results
on condition 1100oC sintering temperature, with the density = 3.82 g/cm3, porosity =
28.21%, phase is formed all BaO.6Fe2O3, have Br = 1804 G and Hc = 933 Oe. |
| Keywords: | Barium-hexa ferrite
sintering
densitas
porositas
kurva histerisis |
| URI: | http://repository.usu.ac.id/handle/123456789/26544 |
| Appears in Collections: | SP - Physics
|
Items in USU-IR are protected by copyright, with all rights reserved, unless otherwise indicated.
|
|